Video Series for – How to handle the fluoride fiber –
■ ZBLAN Fibers
◇Always Stock
■ Non-doped Single Mode Fiber
|
Item
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Cut-off
|
Loss
|
|
–
|
µm
|
µm
|
µm
|
nm
|
dB/m@nm
|
|
| ZSF-6/125-N-0.20 | 0.20±0.01 | 6±1 | 123±3 | 460±30 | <1850 | <0.1@1500 |
| ZSF-6/125-N-0.26 | 0.26±0.01 | 6±1 | 123±3 | 460±30 | <2400 | <0.1@1500 |
|
0.20±0.01
|
7.5±1
|
123±3
|
460±30
|
<2300
|
<0.1@1500
|
|
|
0.26±0.01
|
7.5±1
|
123±3
|
460±30
|
<2900
|
<0.1@1500
|
|
|
0.20±0.01
|
9±1
|
123±3
|
460±30
|
<2600
|
<0.1@1500
|
|
| ZSF-9/125-N-0.26 | 0.26±0.01 | 9±1 | 123±3 | 460±30 | <3450 | <0.1@1500 |
■ Non-doped Multi Mode Fibers
|
Item
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Loss
|
|
µm
|
µm
|
µm
|
dB/m@nm
|
||
|
0.29±0.01
|
95±5
|
123±5
|
450±30
|
<0.1@2500
|
|
|
0.29±0.01
|
160±10
|
200±10
|
480±30
|
<0.1@2500
|
|
|
0.29±0.01
|
400±25
|
500±25
|
600±30
|
<0.1@2500
|
■ Double Cladding Fibers
|
Item
|
Dopant
|
Concentration
|
Core dia.
|
1st Cladding
configuration |
2nd Cladding dia.
|
Absorption
|
|
ppm mol
|
µm
|
µm
|
µm
|
dB/m
|
||
|
ZDF-16/250-10E-C
|
Er
|
10,000
|
16±2
|
250/Circular
|
460
|
0.8 @980nm
|
|
ZDF-18/250-60E-C
|
Er
|
60,000
|
18±3
|
250/Circular
|
460±30
|
2.3 @980nm
|
|
ZDF-18/250-60E-O
|
Er
|
60,000
|
18±3
|
250/Octagon
|
460±30
|
3.6 @980nm
|
|
ZDF-18/330-60E-O
|
Er
|
60,000
|
18±3
|
330/Octagon
|
460±30
|
2~3 @980nm
|
|
ZDF-20/200-60E-O
|
Er
|
60,000
|
20±2
|
200/Octagon
|
430±30
|
4~5 @980nm
|
|
ZDF-30/300-60E-C
|
Er
|
60,000
|
30±3
|
300/Circular
|
460±30
|
–
|
|
ZDF-30/300-60E-O
|
Er
|
60,000
|
30±4
|
300/Octagon
|
425±30
|
2.3 @980nm
|
|
ZDF-7/125-40T-C
|
Tm
|
40,000
|
7±1.5
|
123/Circular
|
200±10
|
1.8 @790nm
|
|
ZDF-7.5/125-40T-C
|
Tm
|
40,000
|
7.5±1.5
|
120/Circular
|
215±10
|
2.1 @790nm
|
|
ZDF-8.5/125-2Ho40T-C
|
Ho/Tm
|
2,000/40,000
|
8.5±2
|
123/Cicular
|
195±15
|
1.5 @800nm
|
◇Current Stock
■ Single Mode Fibers
|
Item
|
Dopant
|
Concentration
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Cut-off
|
Loss Spectrum
|
|
ppm mol
|
–
|
µm
|
µm
|
µm
|
nm
|
|||
|
ZSF-3/125-N-0.25
|
non
|
–
|
0.25
|
3±1
|
123±3
|
450±30
|
<2350
|
|
|
ZSF-9/125-N-0.18
|
non
|
–
|
0.19
|
9±1
|
123±3
|
450±30
|
<2350
|
|
|
ZSF-2.3/120-3.2T
|
Tm
|
3,200
|
0.26
|
2.3±0.5
|
120±4
|
370±30
|
<950
|
|
|
ZSF-2.5/125-4.4T
|
Tm
|
4,400
|
0.27
|
2.5±0.3
|
123±3
|
450±30
|
<1000
|
–
|
|
ZSF-2.7/125-3.2T
|
Tm
|
3,200
|
0.26
|
2.7±0.3
|
123±3
|
450±30
|
<1050
|
|
| ZSF-8.5/125-13T | Tm | 13,000 | 0.16 | 8.5±1.5 | 125±3 | 450±30 | <2200 | click here |
|
ZSF-2.4/125-1.5P
|
Pr
|
1,500
|
0.25
|
2.4±0.4
|
123±3
|
450±30
|
<950
|
|
|
ZSF-4.7/125-2E
|
Er
|
2,000
|
0.20
|
4.7±0.5
|
123±3
|
450±30
|
<1350
|
– |
|
ZSF-5.5/125-5E
|
Er
|
5,000
|
0.12
|
5.5±0.5
|
123±3
|
450±30
|
<950
|
|
|
ZSF-9.0/125-1H
|
Ho
|
1,000
|
0.16
|
9.0±1.0
|
123±3
|
450±30
|
<2100
|
|
|
ZSF-10/125-1H
|
Ho
|
1,000
|
0.16
|
10±5
|
123±3
|
450±30
|
<3150
|
|
|
ZSF-2.1/125-1Y
|
Yb
|
1,000
|
0.28
|
2.1±0.3
|
123±3
|
450±30
|
<900
|
|
|
ZSF-13/125-1D-0.16
|
Dy
|
1,000
|
0.16
|
13±3
|
123±3
|
450±30
|
<3300
|
|
|
ZSF-14/125-3D-0.16
|
Dy
|
3,000
|
0.16
|
14±6
|
123±3
|
475±4
|
<4200
|
|
|
ZSF-13/125-40C
|
Ce
|
40,000
|
0.12
|
13±2
|
123±3
|
450±30
|
<2350
|
■ PM (ellipsoidal core)-Single Mode Fibers
|
Item
|
Dopant
|
Concentration
|
Extinction ratio
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Cut-off
|
Loss Spectrum
|
|
ppm mol
|
dB
|
µm
|
µm
|
µm
|
nm
|
|||
| ZSF-2.2×5.5/125-N-PM | non |
–
|
>20@1.3μm
|
2.2×5.5
|
123±3
|
450±30
|
<1500
|
■ Multi Mode Fibers
|
Item
|
Dopant
|
Concentration
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Loss Spectrum
|
|
ppm mol
|
µm
|
µm
|
µm
|
||||
|
ZMF-90/125-N-0.27
|
non
|
–
|
0.27±0.01
|
90±5
|
123±6
|
460±30
|
|
|
ZMF-100/125-N-0.27
|
non
|
–
|
0.27±0.01
|
95±5
|
123±5
|
460±30
|
|
|
ZMF-145/200-N-0.29
|
non
|
–
|
0.29±0.01
|
145±5
|
200±10
|
480±30
|
|
|
ZMF-152/200-N-0.27
|
non
|
–
|
0.27±0.01
|
152±12
|
200±10
|
480±30
|
|
|
ZMF-395/500-N-0.27
|
non
|
–
|
0.27±0.01
|
395±35
|
500±25
|
600±30
|
■ Double Cladding Fibers
|
Item
|
Dopant
|
Concentration
|
Core dia.
|
1st Cladding
configuration |
2nd Cladding dia.
|
Loss Spectrum
|
|
ppm mol
|
µm
|
µm
|
µm
|
|||
|
ZDF-10/125-N-C
|
non
|
–
|
10±1
|
120/Cicular
|
210±10
|
|
|
ZDF-4.7/125-5E-C
|
Er
|
5,000
|
4.7±0.7
|
124/Cicular
|
210±10
|
|
|
ZDF-15/125-60E-C
|
Er
|
60,000
|
15±2
|
123/Cicular
|
210±10
|
–
|
| ZDF-7.5/125-20T-C | Tm | 20,000 | 7.5±1.5 | 120/Circular | 215±10 | click here |
| ZDF-7.5/125-30T-C | Tm | 30,000 | 7.5±1.5 | 120/Circular | 215±10 | click here |
| ZDF-7.5/125-35T-C | Tm | 35,000 | 7.5±1.5 | 120/Circular | 215±10 | click here |
|
ZDF-10/125-20H-C
|
Ho
|
20,000
|
10±1
|
124/Circular
|
200±10
|
|
| ZDF-10/125-30H2.5P-C | Ho/Pr | 30,000/2,500 | 10±1 | 123/Octagonal | 185±15 | click here |
| ZDF-13/125-30H2.5P-O | Ho/Pr | 30,000/2,500 | 13±1 | 125/Octagonal | 210±10 | – |
| ZDF-3/125-33.7Tb-C | Tb | 33,700 | 3±0.6 | 123/Circular | 200±10 | – |
◇ Always in Stock
■ Non-doped Multi Mode Fibers
|
Item
|
NA
|
Core dia.
|
Cladding dia.
|
Coating dia.
|
Loss
|
|
µm
|
µm
|
µm
|
dB/m@nm
|
||
|
0.22±0.02
|
200±10
|
240±10
|
480±30
|
<0.1@2900
|
|
|
0.22±0.02
|
300±20
|
330±10
|
480±30
|
<0.1@2900
|
|
|
0.22±0.02
|
440±20
|
480±10
|
600±30
|
<0.1@2900
|